PENGUJIAN KUAT TEKAN DAN KUAT LENTUR BALOK LAMINASI KOMBINASI BAMBU PETUNG (DENDROCALAMUS ASPER) DAN KAYU KAPUK RANDU (CEIBA PENTADRA) SEBAGAI BAHAN KONSTRUKSI ALTERNATIF
DOI:
https://doi.org/10.32795/k004a059Keywords:
laminated beam, bamboo petung, kapuk randu, compressive strength, bending strengthAbstract
The demand for wood as a construction material continues to increase in line with the growth of the industrial and development sectors. However, the limited availability of timber due to deforestation and forest degradation demands a more sustainable material alternative. This study aims to find out and compare the values of compressive strength and flexural strength of laminated blocks made of petung bamboo, kapuk randu wood, and a combination of both. The method used was a laboratory experiment with mechanical testing of three groups of laminated beams, each consisting of three specimens. Testing is carried out after the block reaches the age of 7 days. The test results showed that the petung bamboo (BP) beams had an average compressive strength value of 26 MPa and an average flexural strength of 118.56 MPa, making it the group with the highest mechanical performance. The kapuk randu (KR) beam showed the lowest value in both parameters, with a compressive strength of 4 MPa and a bending strength of 27.36 MPa. The combination group of petung-kapuk randu bamboo (KMB) is somewhere in between, with an average compressive strength of 12 MPa and a flexural strength of 53.20 MPa. BP-2 and KMB-2 specimens showed optimal performance in each group. Based on these results, petung bamboo is proven to have high potential as an environmentally friendly construction material, both singly and in combination. The lamination technique on this material can increase mechanical strength and offer a sustainable alternative to the use of conventional wood.
References
Agung. (2015). Teknologi Produksi Laminasi. 1–17.
Astika, I. M. J. (2020). Alfaselulosa Kapuk Randu (A. Wijaya (ed.)). Brilian Internasional. Buku Alfaselulosa Kapuk Randu.pdf
Aulia, M., & Syech, B. (2021). Mengenal Material Bambu Dan Pengaplikasiannya Pada Bangunan.
Badan Standardisasi Nasional. (2013). SNI 7973:2013 Tentang Spesifikasi Desain Untuk Konstruksi Kayu.
Belatrix, N. N., Arnandha, Y., & Firmansyah, D. (2022). Analisis Sifat Mekanik Lentur Papan LaminasiKombinasi Bambu Petung dan Bambu Ater.pdf.
Dewi, S. M., Munawir, A., Murti, W., & Nurlalinah, D. (2017). Bambu Konstruksi Untuk Rakyat. UB Press.
Effendy, R. (2023). Keunggulan Bambu Petung.
Eratodi, I. G. L. B. (2017). Struktur Dan Rekayasa Bambu. In Universitas Pendidikan Nasional (Vol. 1, Issue 1).
Ghulam Rifqi, M., Shofi, M., Amin, U., Rahimi Bachtiar, R., Suryani, E., Murdani, R., Teknik Sipil, J., Studi D-III Teknik Sipil, P., Negeri Banyuwangi Jl Raya Jember, P. K., Kabat, K., Banyuwangi, K., Timur, J., & Studi D-IV Agribisnis, P. (2022). Karakteristik Bambu Ater Banyuwangi Sebagai Laminasi Susunan Lurus Berdasarkan Kuat Tekan dan Kuat Lentur. Jurnal Teknik Sipil, 11(1), 2022–2040.
Hartiyono. (2013). Metode pengawetan kayu. July.
Hilmi, R. Z., Hurriyati, R., & Lisnawati. (2018). Modifikasi Perencanaan Struktur Gedung Apartemen Brooklyn Alam Sutera Menggunakan Struktur Komposit Baja-Beton Dengan Sistem Rangka Berpengaku Eksentris. 3(2), 91–102.
Magang Alam LindungiHutan. (2022, November 20). Mengenal Pohon Randu
Maharani, P. S., & Faimun, F. (2019). Modifikasi Perencanaan Struktur Gedung Grand Dharmahusada Lagoon Menggunakan Struktur Komposit Baja Beton CFT dengan Sistem Rangka Bresing Eksentris Tipe Two-Story-X Braced. Jurnal Teknik ITS, 8(1).
Manik, P., Jokosisworo, S., & Sadewo, G. (2017). Pengaruh Suhu Kempa Terhadap Kualitas Balok Laminasi Kombinasi Bambu Petung Dengan Bambu Apus Untuk Komponen Kapal. Kapal: Jurnal Ilmu Pengetahuan Dan Teknologi Kelautan, 14(1), 7–13.
Novia, S. (2016). Kayu laminasi.
Oka, G. M. (2008). Analisis arah laminasi vertikal dan horisontal terhadap perilaku lentur balok bambu laminasi. Jurnal Smartek, Vol. 6, hal 94-103.
Prasetyo, T. F., Isdiana, A. F., & Sujadi, H. (2019). Implementasi Alat Pendeteksi Kadar Air pada Bahan Pangan Berbasis Internet Of Things. SMARTICS Journal, 5(2), 81–96.
Pratiwi, R. H. (2014). Dalam Penyediaan Obat Herbal. E-Journal Widya Kesehatan Dan Lingkungan, 1, 53–60.
Purwanto, D. (2010). Balok Laminasi Dari Kayu Kelapa (Cocos nucifera L). Jurnal Riset Industri Hasil Hutan
Rahma, M. (2023). Pengaruh Penambahan Limbah Plastik Botol Air Mineral Terhadap Kuat Tekan, Kuat Tarik dan Kuat Lentur Beton. 2(1), 41–49.
Randi, A., Kunci, K., & Sipil, : (2024). Penggunaan Material Komposit dalam Konstruksi Bangunan Bertingkat Tinggi: Kelebihan dan Tantangan. 1–12.
Sajid, I. (2023). Studi alternatif perencanaan struktur komposit pada pembangunan rumah sakit islam ahmad yani surabaya.
Septianto, A., Rakhmawati, A., & Murtopo, A. (2022). Kuat Lentur Balok Laminasi Variasi Kombinasi Bambu Petung dan Apus Menggunakan Lem Kayu Epoxy. 1–5.
Setyo H., N. I., Satyarno, I., Sulistyo, D., & Prayitno, T. A. (2014). Sifat Mekanika Bambu Petung Laminasi. Dinamika Rekayasa, 10(1), 6–13.
Somadona, S., Sribudiani, E., & Elsa Valencia, D. (2020). Karakteristik Balok Laminasi Kayu Akasia (Acacia Mangium) Dan Meranti Merah (Shorea Leprosula) Berdasarkan Susunan Lamina Dan Berat Labur Perekat Styrofoam. Wahana Forestra: Jurnal Kehutanan, 15(2), 53–64.
Suardika, I. M. A. Y., Widnyana, I. N. S., & Artana, I. W. (2023). Balok Laminasi Kombinasi Bambu Petung ( Dendroclamus Asper ) Dan Bambu Ater ( Gigantochloa Atter ) Sebagai Bahan Konstruksi Alternatif. Widya Teknik, 19(1), 55–63.
Tri Wulandari, F. (2019). Karateristik dan Sifat Fisik Bambu Petung (Dendrocalamus asper. Backer) di Kawasan Hutan Kemasyarakatan (HKM) Desa Aik Bual, Provinsi Nusa Tenggara Barat. Buletin Loupe, 15(01), 6.
Wibowo, P. S. (2005). Pemanfaatan laminasi bambu pada konstruksi rumah sederhana. Universitas Islam Indonesia, 8–10.
Wulandari, F. T., & Amin, R. (2024). Karateristik Sifat Fisika Dan Mekanika Papan Laminasi Kombinasi Kayu Rajumas Bambu Petung, Kayu Kemiri Bambu Petung Dan Papan Laminasi Bambu Petung. 5, 1–15.
Wulandari, F. T., Sari, D. P., Ningsih, R. V., & Raehnayati, R. (2023). Pengaruh Tekanan Kempa Papan Laminasi Kayu Sengon dan Bambu Petung. Empiricism Journal, 4(2), 471–477.
Downloads
Published
Issue
Section
License
Copyright (c) 2025 Widya Teknik
This work is licensed under a Creative Commons Attribution 4.0 International License.